High Tensile Strength
Elevator Belts

In elevators; belts, Buckets, and Bolts are important spare parts. In production lines, Elevators have different duties. During the selection of belts working environment, product to be pulled, speed, etc. factors must be taken into consideration. To provide strength, the EP Cord fabric quality must be selected correctly and whether it provides the necessary strength or not. And also working temperature, oil resist, open or closed edges, etc points are the most important. As PlastAgri, we suggest the right Belts for elevators and provide desired length from 100mm to 1000mm in sizes and lengths.

  • Oil Resistant
  • Cut & Closed Edged
  • Speacial Coated Belts
  • Heat Resist Belts
  • EP Cord Fabric Belts
  • Anti-Static Belts

Technical Details

Production Standard

ISO 14890 DIN 22102 and 22104

Cord FabricNylon / Polyester
Belt Weight~ 11 kg/m
Rubber QualityISO 37 ≤17 MPA
Breaking Strength

>= 20 N/mm

Abrasion<= 130 mm
Coating Density1,50 ± 0,3 gram/cm
Heat Resistance-45 till 130C
Width

EN ISO 1000 +/- 1% mm

ThicknessEN ISO 583 12 +/- 10% mm
Plies4-5-6
Breaking StrengthEN ISO 283  ≥1000 kN/m
Elongation at BreakEN ISO 283 ≥10
Maximum ElongationEN ISO 583 ≤1,5 %
Fabric Type

EP125-160-200

Breaking Strength – Warpmin. 200 N/mm
Breaking Strength – Weftmin.N/mm100
Cover Coating ThicknessEN ISO 5832+1/-0,3mm
Under Coating Thickness

EN ISO 583 2+1/-0,2mm

Elongation at BreakISO 37 450%
HardnessISO 7619-1      65 +/- 5ShA
HolesAny
Intensity

ISO 2781+AC1 1,14 +/- 0,02g/m³

Upper Cover/Cord FabricEN ISO 252 ≥ 10,00N/m³
Between PliesEN ISO 252 ≥ 12,00N/m³
Under Cover/Cord FabricEN ISO 252 ≥10,00 N/mm
Temperature Range-40 / +110
Edge CoatingOpen Edge – Closed Edge

Belt Types

EPStrengthPliesCoating

Thickness

125630 kg/cm²51,5+1,5 mm

9 mm

125750 kg/cm²61,5+1,5 mm

10 mm

160800 kg/cm²51,5+1,5 mm

10 mm

160960 kg/cm²61,5+1,5 mm

11 mm

2001000 kg/cm²51,5+1,5 mm

11 mm

2001200 kg/cm²61,5+1,5 mm

12 mm